          環保型70℃阻燃絕緣料 W-7003
          70℃ Lead-free Flame Retardant Insulation Compound...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Product Description產品描述
          W-7003 series are granular compounds which are manufactured through mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw materials, and add plasticizer, stabilizer and other accessory ingredients.
          W-7003系列產品是以優質聚氯乙烯樹脂為基料,加入增塑劑、穩定劑、阻燃劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
           
          Characteristics and Application 特點及用途
          These products have good mechanical and physical property, electrical property and excellent processing performance. They meet RoHS Standard and all their properties comply with GB/T 8815. They are suitable for the insulation of cables which have 70℃and flame retardant requirements.
          產品具有良好的機械物理性能和電性能,加工性能優異,符合RoHS環保標準。性能符合GB/T 8815的要求,主要用于70℃耐溫等級并有阻燃要求的電線電纜絕緣。
           
          Processing Indicator加工工藝
          Recommend to use single-screw extruders with L/D= 20-25.
          建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          Molding Temperature
          機頭溫度
          W-7003 150-175℃ 170-185℃
           

          Physical and Electrical Properties
          機械物理性能及電性能指標

          Item

          試驗項目

          Unit
          單位
          Technical Requirements
          技術要求
          W-7003 W-7003-F5 W-7003-F6
          Oxygen Index
          氧指數
          % ≥30 ≥32 ≥34
          Tensile Strength
          拉伸強度
          MPa ≥15.0 ≥15.0 ≥15.0
          Elongation at Break
          斷裂伸長率
          % ≥150 ≥150 ≥150
          Thermal Deformation
          熱變形
          % ≤40 ≤40 ≤40
          Brittle Temperature with Impact
          沖擊脆化溫度
          -15 -15 -15
          200℃Thermal Stability
          200℃時熱穩定時間
          min ≥60 ≥60 ≥60
          20℃Volume Resistivity
          20℃時體積電阻率
          Ω.m ≥1.0×1012 ≥1.0×1012 ≥1.0×1012
          Dielectric Strength
          介電強度
          MV/m ≥20 ≥20 ≥20
          70℃Volume Resistivity
          70℃時體積電阻率
          Ω.m ≥1.0×109 ≥1.0×109 ≥1.0×109
          Thermal Aging
          熱老化試驗
          \ 100±2℃×168h
          Tensile Strength After Aging
          老化后拉伸強度
          MPa ≥15.0 ≥15.0 ≥15.0
          Tensile Strength Variation
          拉伸強度變化率
          % ±20 ±20 ±20
          Elongation After Aging
          老化后斷裂伸長率
          % ≥150 ≥150 ≥150
          Elongation Variation
          斷裂伸長率變化率
          % ±20 ±20 ±20
          Mass Losses
          質量損失(100℃×168h)
          g/m2 ≤20 ≤20 ≤20
          HCl Gas Evolution
          HCl氣體發生量*
          mg/g ≤100 ≤100 ≤100
          SmokeDensity - flamemode
          煙密度-有焰模式*
          Ds max ≤300 ≤300 ≤300
           

          * When there are low-smoke and low-halogen requirements對產品有低煙低鹵要求時。