          EPDM/PP熱塑性彈性體 EP-3000
          Thermoplastic EPDM/PP Elastomeric Compound...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Product Description 產品描述
          EP-3000 series are dynamic vulcanized compound by EPDM and PP. It is also called thermoplastic TPV. They has various excellent properties such as good climate-resistant (UV, ozone, sunshine, rain), anti-aging, anti-moisture, chemical resistant (acid, alkali, alcohol, ether) and electrical property. Their cold-resistant property is very well and can be worked in -40℃~125℃for long time. EP-3002 and EP-3003 are medium level oil-resistant. The hardness of the series can reach 75A-40D.
          EP-3000是三元乙丙膠與聚丙烯(EPDM/PP)的動態硫化共混物,又稱熱塑性硫化橡膠(TPV),具有硫化橡膠的各種優異性能,有卓越的耐侯性(紫外線,臭氧,日光,雨水)耐老化,耐水性,耐化學品(酸、堿、醇、醚)和電性能。耐低溫性能卓越,能在-40℃~125℃的溫度中長期工作。其中3002和3003有中等耐油性。硬度范圍可以做到:75A-40D。
           
          Product Application 產品用途
          l  Insulation and jacketing of DC control cables, rail cables
          l  Insulation and jacketing of port machine cables, vessel cables and high-voltage submarine cables
          l  Injection mold parts of cables and jacketing of container lorry cables
          l  Car rubber parts: seal, exhaust pipes and interior decoration parts
          l  Water-proof coiled material of architecture, seal of refrigerator
          l  直流控制電纜,軌道交通電纜絕緣和護套
          l  港機和船用電纜,高壓海底電纜的絕緣和護套
          l  電纜注塑件,集卡電纜護套
          l  汽車橡膠件:密封條,排風管,內飾件等
          l  建筑用防水卷材,冰箱密封條
           
          Process Condition 加工要求
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          MoldingTemperature
          機頭溫度
          Melt Temperature
          熔體溫度
          EP-3000 150 ℃– 190 ℃ 195 ±5℃ 185±5℃
          Above data is just for your reference and need to be adjusted according to the actual situation.
          以上加工條件只是參考,具體需根據實際情況做適當調整。
           
          Dry Condition 干燥條件
          No need for drying in normal environment. If the compound was affected with damp, dry it under 90℃conditions for 2-3 hours or under 70-80℃conditions for 3-4 hours. Keep the moisture content smaller than 0.1wt%.
          一般不需干燥。如受潮,在90℃條件下干燥2-3小時,或在70-80℃條件下干燥3-4小時,保持樹脂含水量小于0.1wt%后再使用。
           
          Physical and Electrical Properties   物理及電氣性能
          Item
          試驗項目
          Unit
          單位
          Typical Data典型值
          EP-3001 EP-3002 EP-3003
          Density at 23℃  23℃密度 g/cm3 0.918 1.09 0.95
          Hardness  硬度 Share A 92 90 87
          Melt Flow Index 熔體流動速率2.16kg×210℃ g/10min 0.39 0.52 ----
          Tensile Strength  拉伸強度 MPa 17 15.2 10.2
          Spring Back  回彈性 % 43 38 32
          Elongation at Break  斷裂伸長率 % 542 460 185
          Break Set  扯斷永久變形 % 104 ---- ----
          Compression Set
          壓縮永久變形
          70℃×22hr % 37.5 ---- ----
          100℃×22hr % 42 ---- ----
          Abrasion
          磨耗量(阿克。
          cm3/1.61kM 0.96 0.62 ----
          Ozone Resistance Aging
          耐臭氧老化
          50×10-8
          Tension 20%
          40℃×72hr
          No crake
          無裂紋
          No crake
          無裂紋
          No crake
          無裂紋
          Low Temperature Impact
          低溫沖擊
          -30℃ Pass
          通過
          Pass
          通過
          Pass
          通過
          Brittleness Temperature
          脆性溫度
          -50 -44 -45.5
          Air Aging Condition
          熱空氣老化條件
          150℃×168h
          Variation of Tensile Strength
          拉伸強度變化率
          % +18.3 +25.5 +15.5
          Variation of Elongation
          斷裂伸長變化率
          % -13.7 -14.2 -17.1
          Volume Resistivity 體積電阻率 Ω.m 4×1012 2.5×1012 ----
          耐油性能
          Oil Resistance Properties
           
          ASTM 1# Oil
          70℃x168h
          Retention of Tensile Strength
          拉伸強度保持率
          % ---- 80 78
          Retention of Elongation伸長率保持率 % ---- 79 74
          Variation of Volume
          體積變化率
          % ---- +8.5 +9.6
          耐油性能
          Oil Resistance Properties
           
          ASTM 2# Oil
          120℃x24h
          Retention of Tensile Strength
          拉伸強度保持率
          % ---- 51.6 53
          Retention of Elongation
          伸長率保持率
          % ---- 32.2 31.5
          Variation of Volume
          體積變化率
          % ---- 76 72