          您所在的位置:網站首頁 > > 產品中心 > XLPE絕緣材料 > 低煙無鹵電纜料125℃低煙無鹵阻燃熱塑性彈性體 TEWR125
          125℃低煙無鹵阻燃熱塑性彈性體 TEWR125
          125℃Thermoplastic Low-smoke Halogen-free Flame-retardant Elastomeric Compound ...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Description and Application 產品描述和用途
          TEWR125 is a kind of thermoplastic low-smoke halogen-free flame-retardant elastomeric compounds. The highest working temperature is 125℃. It has good mechanical property, electrical property, flame retardant property as well as processability. Its high-temperature resistant aging property is very well and suitable for strict aging requirements of insulation and jacketing. It also can be used for other cables which have long service life requirements. It is simple processing without cross-linking and can be recycled.
          TEWR125是一種低煙無鹵阻燃熱塑性彈性體,其具有優良的物理機械性能,電性能,阻燃性能以及加工性能,更為突出的是其具有卓越的耐高溫老化性能,特別適用于對老化條件要求較高的絕緣,護套上,也可用于其它有較長使用壽命要求的電纜上。產品無需交聯,加工工藝簡單,環?苫厥。最高使用溫度為125℃。
           
          Processing Indicator 加工工藝
          Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
          采用低煙無鹵專用螺桿,長徑比L/D=20-25。
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          Molding Temprature
          機頭溫度
          TEWR125 130-125℃ 150-165℃
           
          Physical and Electrical Properties 物理及電性能指標
          Item
          試驗項目
          Unit
          單位
          Specification
          技術要求
          Density
          密度
          g/cm3 ≤1.45
          Tensile Strength
          拉伸強度
          MPa ≥10
          Elongation at Break
          斷裂伸長率
          % ≥180
          Aging Conditions
          空氣熱老化條件
          / 158℃×168h
          Reserved Tensile Strength
          拉伸強度保留率
          % ≥70
          Reserved Elongation at Break
          斷裂伸長率保留率
          % ≥70
          Dielectric Strength
          介電強度
          MV/m ≥20
          Brittle Temperature With Low Temperature Impact
          沖擊脆化溫度
          -40
          20℃Volume Resistivity
          20℃體積電阻率
          Ω. m ≥1.0×1012
          Oxygen Index
          氧指數
          % ≥28
          HCL Gas Evolution
          HCL氣體發生量
          Mg/g ≤5.0
          PH Value
          PH值
          / ≥4.3
          Smoke Density煙密度
          – No-flame Mode無焰模式
          – Flame Mode有焰模式
          Ds max  
          ≤200
          ≤100
          Conductivity
          電導率
          uS/mm ≤10
          Toxicity Index
          毒性指數
          / ≤5.0