          抗開裂低煙無鹵聚烯烴阻燃護套料 EHW90K
          Cracking Resistant Low-smoke Halogen-free Flame-retardant Polyolefin Jacketing Compound ...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Description and Application  產品描述和用途
          EHW90K is 90℃cracking resistant low-smoke halogen-free flame-retardant jacketing compound, which doesn’t contain any heavy metals like Pb, Ba, Cd, Cr, Sn and Sb. The properties can meet RoHS Standard. It has excellent physical and mechanical properties, especially good thermal-shock resistant performance. Its temperature resistant is from -40 ℃to 90℃and mainly used for communication cables, control cables and power cables, which have strict cracking-resistant requirements.
          EHW90K是90℃抗開裂低煙無鹵阻燃護套料。產品具有優異的物理機械性能尤其是具有較好的抗熱沖擊能力,低溫可耐-40℃,最高使用溫度為90℃。主要用于抗開裂性要求較高的通信電纜,控制電纜和電力電纜的護套層。環保方面,產品不含Pb、Ba、Cd、Cr、Sn、Sb六大重金屬,其性能均能滿足RoHS的標準要求。
           
          Processing Indicator加工工藝
          Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
          采用低煙無鹵專用螺桿,長徑比L/D=20-25。
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          Molding Temprature
          機頭溫度
          EHW90K 130-140℃ 145-155℃
           
          Physical and Electrical Properties   物理及電性能指標
          Item
          試驗項目
          Unit
          單位
          Specification
          技術要求
          Density
          密度
          g/cm3 ≤1.45
          Tensile Strength
          拉伸強度
          MPa ≥10
          Elongation at Break
          斷裂伸長率
          % ≥150
          Aging Conditions
          熱老化條件
          / 110℃×240h
          Tensile Strength Variation
          拉伸強度變化率
          % ±25
          Elongation Variation
          斷裂伸長率變化率
          % ±25
          Thermal
          Deformation
          熱變形
          Condition 90℃×6h
          Variation % ≤50
          Dielectric Strength
          介電強度
          MV/m ≥20
          Brittle Temperature With Low Temperature Impact
          沖擊脆化溫度
          -40
          20℃Volume Resistivity
          20℃體積電阻率
          Ω.m ≥1.0×1011
          Oxygen Index
          氧指數
          % ≥30
          Heat Shock
          熱沖擊實驗(150℃×1h)
          / 不開裂
          HCL Gas Evolution
          HCL氣體發生量
          Mg/g ≤1.0
          PH Value  
          PH值
          / ≥4.3
          Smoke Density煙密度
             – No Flame Mode 無焰模式
          – Flame Mode有焰模式
          Ds max ≤200
          ≤150
          Conductivity
          電導率
          uS/mm ≤10
          Toxicity Index
          毒性指數
          / ≤5.0