          125℃一步法硅烷交聯彈性體絕緣料 GXT-125
          125℃ One-step Silane Cross-linkable Elastomeric Compound...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Product description 產品描述和用途
          GXT-125 is one-step silan cross-linkable polyolene insulation compound for low-voltage cables. It is a kind of insulations of low-voltage cables and control cables through squeeze tube mold production process. Cable working voltage is 10KV and below, the highest working temperature is 125℃.
          GXT-125是低壓電線電纜用一步法硅烷交聯聚乙烯絕緣料。主要用于通過擠管式模具生產的低壓電力電纜和控制電纜的絕緣。電纜工作電壓為10KV以下,最高工作溫度為125℃。
           
          Processing Indicator 加工工藝  
          Recommend to process with the PE extruder.
          建議使用聚乙烯專用擠出機進行加工。
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          Molding Temprature
          模頭溫度
          GXT-125 160-210℃ 215-220℃
           
           
           
           
          Physical and Electrical Properties 物理和電氣性能
          Item
          試驗項目
          Unit
          單位
          Technical requirements
          技術要求
          Density
          密度
          g/cm3 0.922±0.005
          Tensile Strength
          拉伸強度
          MPa ≥13.5
          Elongation at Break
          斷裂伸長率
          % ≥3450
          Hardness
          硬度(shoreA)
          ---- ≤88
          Brittle Temperature with Low Temperature
          低溫脆化溫度

          失效數
          -76
          ≤15/30
          20℃Volume Resistivity
          20℃體積電阻率
          Ω·m ≥1.0×1014
          20℃Dielectric Strength,50Hz
          20℃介電強度, 50Hz
          MV/m ≥25.0
          20℃Dielectric Constant,50Hz
          20℃介電常數, 50Hz
          ---- ≤2.35
          Air Aging Condition
          熱空氣老化條件
          158±2℃×168h
          Tensile Strength Variation After Aging
          拉伸強度變化率
          % ±25
          Elongation Variation After Aging
          斷裂伸長變化率
          % ±25
          Hot Set Test Condition
          熱延伸試驗條件
          200℃×0.2MPa×15min
          1mmthick 95 ℃ boiled 2 hours test 1mm厚95℃水煮
          2小時測試
          Hot Elongation
          負荷下伸長率
          % ≤100
          Permanent Deformation after Cooling
          冷卻后永久形變
          % ≤5